Process for the preparation of vanadyl sulfate solution

ABSTRACT

A process for producing a vanadyl sulphate solution (VOSO4) comprises forming a suspension of vanadium trioxide (V2O3) in a sulphuric acid solution and contacting the V2O3 suspension with a strong oxidising agent under controlled conditions to produce the VOSO4 solution. A preferred oxidising agent is hydrogen peroxide, which is added very slowly to the V2O3 suspension due to the violent nature of the reaction.

BACKGROUND TO THE INVENTION

THIS invention relates to a process for the preparation of a vanadyl sulphate solution.

It is known to produce vanadyl sulphate by dissolving vanadium pentoxide in hot dilute sulphuric acid under vigorous agitation and continued heating with the aid of sulphur dioxide as a reducing agent.

The limited solubility of sulphur dioxide in acidic and aqueous solutions results in the emission of sulphur dioxide from the solution and this presents an environmental hazard. Overdosing of the solution with SO₂ gas results in the unwanted formation of the lower valent vanadium sulphate, namely V₂SO₄ and not vanadyl sulphate (VOSO₄).

Since the dissolution of vanadium pentoxide in sulphuric acid is endothermic heat has to be provided to drive the formation of vanadyl sulphate.

There is thus always a need for a new method for the production of vanadyl sulphate.

SUMMARY OF THE INVENTION

According to the invention a process for producing a vanadyl sulphate solution includes the steps of:

-   (1) providing a starting material comprising vanadium trioxide     (V₂O₃); -   (2) contacting the vanadium trioxide with an appropriate volume and     concentration of a sulphuric acid solution to produce a vanadium     trioxide suspension; and -   (3) contacting the vanadium trioxide suspension with a strong     oxidising agent that is capable of raising the valency or oxidation     state of the vanadium, thereby to dissolve the vanadium trioxide in     the sulphuric acid to produce the vanadyl sulphate solution (VOSO₄).

Various strong oxidising agents including peroxides and permanganate such as hydrogen peroxide, sodium peroxide and potassium permanganate, for example, can be used. Hydrogen peroxide is particularly preferred as it does not introduce any impurities into the final product.

The hydrogen peroxide is typically added slowly to the vanadium trioxide suspension due to the violent nature of the reaction.

BRIEF DESCRIPTION OF THE DRAWING

The invention will now be described in more detail, by way of example only, with reference to the accompanying drawings in which:

FIG. 1 is a graph indicating the mass relationship between varying quality V₂O₃ expressed as V₂O₅ against constant 4.5 g V₂O₅ portions in a 4.0 molar sulphuric acid solution; and

FIG. 2 indicates the reduction potential in mVolt against the mass of the V₂O₃ used.

DESCRIPTION OF A PREFERRED EMBODIMENT

The crux of the invention is to use a strong oxidising agent to dissolve vanadium trioxide (V₂O₃), commonly referred to as Hivox, in a sulphuric acid solution to produce vanadyl sulphate (VOSO₄).

In carrying out the process, a strong oxidising agent such as a peroxide or permanganate, for example, is used to dissolve the V₂O₃ in a warm sulphuric acid solution with constant stirring. Although various strong oxidising agents such as hydrogen peroxide, sodium peroxide, potassium permanganate, iodine, potassium iodate, potassium bromate, bromine, ammonium persulfate, persulfates of sodium and potassium, cerium (IV) sulphate, and potassium dichromate, for example, can be used, hydrogen peroxide is preferred as it does not introduce any impurities into the final product.

As the quality of industrial grade Hivox ranges typically from 115 to 122 percent equivalent V₂O₅, FIG. 1 can be used in order to determine an appropriate quantity of V₂O₃ for use in the process, depending on the quality of the starting material used. The required solution can be obtained by monitoring the reduction potential thereof in mVolt, as shown in FIG. 2, during the dissolution process. The start of production of vanadyl sulphate is illustrated at the point where the graph dips sharply.

The invention will now be illustrated by way of the following non-limiting example.

EXAMPLE

Hydrogen peroxide was used to dissolve 3.0 grams Hivox (V₂O₃) in a warm (50° C.) 4.0 molar sulphuric acid solution with constant stirring. The hydrogen peroxide was added dropwise as it reacted violently with the solution. During the dissolution process the reduction potential of the solution was continuously monitored and the addition of hydrogen peroxide stopped when the solution reached the end point at 600 mVolts.

The process proceeded according to the following formula: 2V₂O₃+4H₂SO₄+H₂O₂→4VOSO₄+4H₂O+H_(2↑).

During the process, the solution first turned green, which is indicative of the presence of V³⁺ ions, whereafter it turned blue, which is indicative of the presence of VO²⁺ ions present in the vanadyl sulphate end product.

From the above, it is evident that vanadyl sulphate can readily be made using Hivox (V₂O₃), which is generally more cost effective, and less hazardous, than the conventional process using V₂O₅. 

1. A process for producing a vanadyl sulphate solution includes the steps of: (1) providing a starting material comprising vanadium trioxide (V₂O₃); (2) contacting the vanadium trioxide with a sulphuric acid solution to produce a vanadium trioxide suspension; and (3) contacting the vanadium trioxide suspension with a strong oxidising agent that is capable of raising the valency or oxidation state of the vanadium, thereby to dissolve the vanadium trioxide in the sulphuric acid to produce the vanadyl sulphate solution (VOSO₄).
 2. A process according to claim 1, wherein the strong oxidising agent is selected from the group comprising hydrogen peroxide, sodium peroxide, potassium permanganate, iodine, potassium iodate, potassium bromate, bromine, ammonium persulfate, persulfates of sodium and potassium, cerium (IV) sulphate, and potassium dichromate
 3. A process according to claim 2, wherein the strong oxidising agent is hydrogen peroxide.
 4. A process according to claim 3, wherein the hydrogen peroxide is added dropwise to the vanadium trioxide suspension.
 5. A process according to claim 4, wherein the addition of hydrogen peroxide is stopped when the reduction potential of the vanadium sulphate solution reaches a predetermined end point.
 6. A process according to claim 5, wherein the end point is at about 600 mVolts. 